Supplier Homepage > Products > PP High Performance V2 Flame Retardant Master Batch (FR-CPP-4)
PP High Performance V2 Flame Retardant Master Batch (FR-CPP-4)
Click on the image to check the artwork
product: view count: 388PP High Performance V2 Flame Retardant Master Batch (FR-CPP-4) 
unit price: Negotiable
min amount:
amount:
period for delivery: Consignment Deadline days
Expiry date: Long Effective
last update: 2017-09-15 02:14
  enquiry
detailed

Introduction

FR-CPP-4 consists of environment friendly flame retardant system of bromine, phosphorus and nitrogen, comply with ROHS requirement. It is not only relies on gas and condensed phases to the dual flame retardant but also takes away heat by melt dripping through the catalytic effect to get flame retardant effect. Advantages: high effective, low smoke, no mold corrosion, high smoothness, low halogen and high cost performance.

Application

Mainly used in PP injection and extrusion, such as: PP receptacle, PP blower, except that, it can be used in PP hollow plate, cast film, non woven fabric, panel, clapboard, enclosure of household appliance, connecter, outdoor flame retardant seat etc. Products.

Index

Item

Index

Appearance

White Granular

Density g/cm3

1.10

Decomposition Temp℃≥

230

Content %>

40

Water Content %≤

0.1

Recommended Dosage

4-6%

Solubility Index g/min,200℃5kg

21.0

Melting Temp ℃≥

160

Extrusion Process (Twin Screw Extruder)

Note: Vacuum when production; Recommended Screw L/D 1:36-40;

Packing/Storage

25KG/bag: Transported as a common chemical and stored in dry and cool place, avoid direct sunlight. 

Appendix:Application Examples

1-1.Formula

Materials

Formula A


PPT30S

100

-

PPJ340

-

100

FR-CPP-4

4

6

Flame Retardancy UL94 3.2/1.6mm

V2

V2

1-2.Technical Data

Properties

Test Methods

Unit

PPT30S

PPJ340

Formula A


Density

ASTMD-792

g/cm3

0.9

0.9

1.0

1.0

Tensile Strength

ASTM-D638

Mpa

31.3

23.3

31.1

24.0

Elongation At Break

ASTM-D638

%

350.6

1006.6

230

308

Flexural Strength

ASTM-D790

Mpa

27.2

19.2

30.3

23.6

Flexural Modulus

ASTM-D790

MPa

980.4

683.5

1260.6

918.5

Izod Impact Strength Notched(23℃)

ASTM-D256

KJ/m2

5.35

55

6.3

51.9

Flame Retardancy 3.2mm

UL94

_

Non flame retardant

Non flame retardant

V2

V2

GWFI

IEC60695-2-12

Non flame retardant

Non flame retardant

875/3.0

875/3.0

Color

-

-

Nature Color

Nature Color

Nature Color

Nature Color

1-3. PP Injection Process:

Drying condition: Drying at 70-75 deg C to 2-3 hours by desiccant dryers.

Injection machine temperature setup:

Heating Zone

Step1

Step2

Step3

Nozzle

Temperature

170

180

190

180

Note:

1. All the application typical data above are just for reference, not an official warranty certificate.

2. Provide different design solutions according to requirement of customers.